[1]王圣程,姜慧,黄兰英,等.利用废弃混凝土制备固碳型充填膏体的技术可行性分析[J].徐州工程学院学报(自然科学版),2020,(03):69-72.
 WANG Shengcheng,JIANG Hui,HUANG Lanying,et al.Technical Feasibility Analysis of Using Waste Concrete to Prepare Carbon Sequestration Paste[J].Journal of Xuzhou Institute of Technology(Natural Sciences Edition),2020,(03):69-72.
点击复制

利用废弃混凝土制备固碳型充填膏体的技术可行性分析()
分享到:

《徐州工程学院学报》(自然科学版)[ISSN:1674-358X/CN:32-1789/N]

卷:
期数:
2020年03期
页码:
69-72
栏目:
工程技术
出版日期:
2020-09-30

文章信息/Info

Title:
Technical Feasibility Analysis of Using Waste Concrete to Prepare Carbon Sequestration Paste
文章编号:
1674-358X(2020)03-0069-04
作者:
王圣程姜慧黄兰英禄利刚张朕
(徐州工程学院 土木工程学院,江苏 徐州221018)
Author(s):
WANG ShengchengJIANG HuiHUANG LanyingLU LigangZHANG Zhen
(School of Civil Engineering,Xuzhou University of Technology,Xuzhou 221018,China)
关键词:
废弃混凝土 粗骨料 细骨料 充填膏体 固碳 性能
Keywords:
waste concrete coarse aggregate fine aggregate filling paste carbon fixation performance
分类号:
TD823
文献标志码:
A
摘要:
针对煤矿充填原料不足、废弃混凝土堆放对环境的破坏及碳排放等问题,研究了废弃混凝土粗、细骨料替代率对充填膏体流动性能、流变性能和力学性能的影响,分析了利用废弃混凝土制备充填膏体进行固碳的可行性,并结合现有研究成果,设计出利用废弃混凝土制备固碳型充填膏体的方法.结果表明:当粗、细骨料替代率为30%~70%时,膏体能满足充填各个环节要求; 当充填膏体固碳率超过20%时,膏体的抗压强度达到蒸汽养护的80%~90%,所需时间仅为45 min,生产周期被大幅度缩短.所设计的方法现实可行,对废弃混凝土的再利用及固碳型充填膏体的研究具有借鉴意义.
Abstract:
In view of the shortage of filling materials in coal mines,the environmental damage caused by the stacking of waste concrete and the carbon emission,this paper studies the influence of the replacement ratio of coarse aggregate and fine aggregate of waste concrete on the flow performance,rheological performance and mechanical performance of filling paste,analyzes the feasibility of using waste concrete to prepare filling paste for carbon fixation,and designs the use of waste concrete based on the existing research results.The results [JP]show that when the replacement rate of coarse and fine aggregate is 30%|70%,[JP]the paste can meet the requirements of filling each link; when the carbon fixation rate of filling paste is more than 20%,the compressive strength of paste reaches 80%|90% of steam curing,the time required is only 45 minutes,and the production cycle is greatly shortened.The design method is practical and feasible,which can be used for reference in the reuse of waste concrete and the research of carbon fixation filling paste.

参考文献/References:

[1] 韩宇峰,殷志祥,郭保立.以建筑垃圾为骨料充填膏体的可行性探究[J].煤炭技术,2018,37(4):24|26.
[2] 冯国瑞,贾学强,郭育霞,等.废弃混凝土粗骨料对充填膏体性能的影响[J].煤炭学报,2015,40(6):1320|1325.
[3] XI F,DAVIS S J,CIAIS P,et al.Substantial global carbon uptake by cement carbonation[J].Nature Geosciences,2016,9(12):880|883.
[4] 贾学强,冯国瑞.废弃混凝土细骨料对矿山充填膏体性能的影响[J].矿业研究与开发,2015,35(11):37|40.
[5] 杨宝贵,韩玉明,杨鹏飞,等.煤矿高浓度胶结充填材料配比研究[J].煤炭科学技术,2014,42(1):30|33.
[6] 董慧珍.采空区充填料浆及其管道输送特性试验研究[D].太原:太原理工大学,2013.
[7] 陈宗平,徐金俊,郑华海,等.再生混凝土基本力学性能试验及应力|应变本构关系[J].建筑材料学报,2013,16(1):24|32.
[8] 邹庆焱.二氧化碳养护混凝土技术研究[D].长沙:中南大学,2008.
[9] 郗凤明,石铁矛,王娇月,等.水泥材料碳汇研究综述[J].气候变化研究进展,2015,11(4):288|296.)
[10] 阮欣,刘栩,陈艾荣.考虑应力状态的二维混凝土碳化过程数值模拟[J].同济大学学报(自然科学版),2013,41(2):191|196.
[11] 石铁矛,周诗文,李绥,等.建筑混凝土全生命周期固碳能力计算方法[J].沈阳建筑大学学报(自然科学版),2015(5):829|837.

备注/Memo

备注/Memo:
收稿日期:2020-03-17
基金项目:(国家自然科学基金项目(51904270); 江苏省高等学校自然科学研究重大项目(19KJA570001); 江苏省建设系统科技项目(2019ZD001066); 徐州工程学院科研项目(XKY2019114))
作者简介:王圣程(1987-),男,讲师,博士,主要从事建筑安全与矿业安全研究.
更新日期/Last Update: 2020-09-30